DETEKSI CACAT SAMPEL LAS MATERIAL SA533-B1 BEJANA TEKAN DENGAN METODA UJI TAK RUSAK

Mudi Haryanto, MH and Sri Nitiswati, SN and Andryansyah, AD and Deswandri, DW and Geni Rina Sunaryo, GRS (2017) DETEKSI CACAT SAMPEL LAS MATERIAL SA533-B1 BEJANA TEKAN DENGAN METODA UJI TAK RUSAK. In: Seminar Nasional Teknologi Energi Nuklir 2017, 12 Oktober 2017, Makassar.

[img]
Preview
Text
Prosiding-SENTEN-2017.pdf

Download (33MB) | Preview

Abstract

ABSTRAK DETEKSI CACATSAMPEL LAS MATERIAL SA533-B1 BEJANA TEKAN DENGAN METODE UJI TAK RUSAK. SA533-B1 adalah materialyang banyak digunakan pada meterial bejana tekan reaktor PWR. Umumnya pembuatan bejana tekan dilakukan dengan sambungan las. Untuk mengetahui kualitas pengelasan perlu dilakukan uji mekanik. Persyaratan sebagai benda uji mekanik adalah pada bagian sampel las dimana akan dibuat benda uji mekanik harus terbebas dari cacat. Sampel las SA533-B1 di las dengan proses SMAW. Tujuannya untuk mengetahui ada/tidaknya cacat las pada daerah sambungan yang di las, sehingga dapat diputuskan kemungkinan dapat/tidaknya sampel uji las dibuat untuk bahan benda uji mekanik.Metoda yang digunakan adalah uji tak rusak terdiri dari metode dye penetrant dan metode ultrasonik. Sampel las disediakan sebanyak 3 buah terdiri dari ukuran (132 x 130 x 12)mm sebanyak 1 buah dan ukuran (300 x 100 x 10)mm sebanyak 2 buah.Hasil dari pengujian dengan metoda dye penetrant dan metoda ultrasonik, pada sampel las nomor 1 ditemukan cacat porositi dipermukaan dan di dalam las, sampel las nomor 2 ditemukan cacat retak dipermukaan dan di dalam las, dan sampel nomor 3 ditemukan cacat lack of side wall fusion di dalam las. Semua cacat-cacat tersebut tidak merata sepanjang sambungan las, sehingga disimpulkan bahwa sampel las dapat dibuat benda uji mekanik pada daerah yang tidak ada cacatnya. Kata kunci : Sampel las SMAW, SA533-B1, bejana tekan, uji tak rusak, uji mekanik ABSTRACT DETECTION OF SA533-B1 MATERIAL WELD SAMPLE OF PRESSURE VESSEL BY NON-DESTRUCTIVE METHOD. SA533-B1 is a material widely used in PWR reactor pressure vessel materials. Generally, the manufacture of pressure vessels made with welded joints. To determine the quality of the welding necessary mechanical tests. The requirement as mechanical specimen that is area of weld sample which is mechanical specimen will be taken should be free from any defects. Weld sample of SA533-B1 has been welded by SMAW process. The purpose of examination is to know whether any defect or not on welded area, so can be decide the possibility weld sample to make it as mechanical specimen. The methods used by non-destructive test such as dye penetrant and ultrasonic methods. Amount of weld samples are 3 pieces consist of 1 sample with dimension of (132 x 130 x 12) mm, and 2 samples with dimension of (300 x 100 x 10) mm. Results of the test by the dye penetrant method and the ultrasonic method, in the welded sample number 1 found porosity defects on the surface and in the weld, the welded sample number 2 found cracked defects on the surface and in the weld, and sample number 3 found defect lack of side wall fusion at in welding. All the defects are uneven throughout the weld joint, so it is concluded that the weld sample can be made mechanical test object in the non-defective area. Keywords: SMAW weld sample, SA533-B1, pressure vessel, non-destructive testing, mechanical testing

Item Type: Conference or Workshop Item (Paper)
Subjects: Keselamatan dan Keamanan Nuklir
Divisions: Pusat Teknologi dan Keselamatan Reaktor Nuklir
Depositing User: USER PTKRN BATAN
Date Deposited: 08 May 2018 03:53
Last Modified: 08 May 2018 03:53
URI: http://repo-nkm.batan.go.id/id/eprint/1154

Actions (login required)

View Item View Item