PENGARUH PENAMBAHAN KONSENTRASI Ag2S TERHADAP KOMPOSIT KONDUKTOR (Ag2S)x(Na3PO4)1-x(x=0,1-0,5)

Safei, Purnama and Patricius, Purwanto and Grace, Tj. Sulungbudi (2016) PENGARUH PENAMBAHAN KONSENTRASI Ag2S TERHADAP KOMPOSIT KONDUKTOR (Ag2S)x(Na3PO4)1-x(x=0,1-0,5). Jurnal Kimia dan Kemasan, 38 (2). pp. 77-84. ISSN 2549-9424

[img] Text
2701 - Published Version
Available under License Creative Commons Attribution Non-commercial Share Alike.

Download (33kB)

Abstract

The conductor composite of (Ag2S)x (Na3PO4)1-x had been made by mixing Ag2S with Na3PO4, then compaction with pressure 48.26.106 N/m2 with diameter 1.5.10-2 m. The conductor composite of (Ag2S)x(Na3PO4)1-x were heated at temperature 150 oC for 5 hours. Determination structure of (Ag2S)x(Na3PO4)1-x by using x-ray diffraction, showed that the structure of (Ag2S)x(Na3PO4)1-x was Ag2S and Na3PO4. Determination of conductivity (Ag2S)x(Na3PO4)1-x was carried out by LCR-meter at the interval frequency 0.1 Hz to 100 kHz. The result showed that the composite conductivity (Ag2S)x(Na3PO4)1-x was increased and impedance decreased with increasing concentration of Ag2S. The surface morphology of composite of (Ag2S)x(Na3PO4)1-x were conducted by electron microscopy, the result showed that take place to change with increasing concentration of Ag2S.

Item Type: Article
Subjects: Daur Bahan Bakar Nuklir dan Bahan Maju > Bahan Struktur dan Bahan Maju > Teknik Sintesis Bahan Maju
Divisions: Pusat Sains dan Teknologi Bahan Maju
Depositing User: EDITOR PSTBM BATAN
Date Deposited: 09 May 2018 02:15
Last Modified: 18 May 2018 03:06
URI: http://repo-nkm.batan.go.id/id/eprint/1174

Actions (login required)

View Item View Item