Rinanti Susilowati, Sri and Riyanto, Sugeng and Husnurrofiq, Dedy (2017) Pembuatan Gel Ceria Stabilized Zirconia metode Gelasi Eksternal. PIN, 10 (19). pp. 1-13. ISSN 1979-2409

[img] Text (Pembuatan Gel Ceria Stabilized Zirconia metode Gelasi Eksternal)
3548

Download (20kB)

Abstract

ABSTRAK –Telah dilakukan pembuatan gel ceria stabilized zirconia (CSZ) dengan metoda gelasi eksternal. Sebagai bahan dasar umpan gelasi menggunakan Ce(NO3)3.6H2O dan ZrO(NO3)2.2H2O dengan perbandingan mol Zr/Ce = 8. Pembuatan umpan gelasi kedua bahan pokok dicampur dilarutkan dalam Air Bebas Mineral (ABM) ditambah zat aditif Polyvinyl Alcohol (PVA) sebagai pengatur viskositas dan Tetra Hydro Furfuryl Alcohol (THFA). Untuk memperoleh gel yang baik, maka parameter kunci yang harus dipenuhi antara lain adalah pH sol, viskositas umpan, frekuensi, amplitude dan flow rate aliran umpan. Proses setelah gelasi eksternal meliputi perendaman, pencucian dan pengeringan serta kalsinasi. Pada proses pencucian, konduktivitas air cucian terakhir dikondisikan pada ≤ 20 µS/cm setara dengan 0,001 % berat kandungan NH4OH, dianggap gel sudah cukup baik untuk dilanjutkan ke proses selanjutnya. Proses pengeringan dilakukan pada kondisi vakum pada 80 oC dan kondisi temperature kamar sedangkan kalsinasi pada suhu 300 oC dan 500 oC dengan laju pemanasan < 2oC pada suasana atmosfer. Gel CSZ hasil pengeringan diukur diameternya dan kondisi fisiknya menggunakan mikroskop digital. Dari hasil pengukuran diameter gel CSZ basah, diameter gel hasil pengeringan adalah 1,0058 mm dan diameter hasil kalsinasi pada suhu 300 oC adalah 0,663 mm serta 500 oC diameternya 0,635 mm. Kondisi fisik gel CSZ hasil pengeringan dan kalsinasi adalah utuh, bulat dan tidak pecah. Kata kunci: sol gel, gelasi ekternal, ceria stabilized zirconia ABSTRACT –The ceria stabilized zirconia (CSZ) gel was prepared with an external gelation method. As starting material Ce (NO3) 3.6H2O and ZrO (NO 3) 2.2H2O with mol ratio Zr to Ce 8. Was Used the broth solution of the two starting materials is mixed dissolved in demineral Water plus additives Polivinyl Alcohol (PVA) it is resulted not not viscosity control and Tetra Hydro Furfural Alcohol (THFA). To obtain a good gel, the key parameters such as pH sol, feed viscosity, frequency, amplitude and flowrate of the feed gelation. After the external gelation aging, washing and drying (AWD), as well as calcination were conducted In the washing process, the last wash in water conductivity is conditioned at ≤20μS / cm equivalent to 0.001% by weight of NH4OH content, which is considered to be sufficiently good to proceed to the next process. The drying process is carried out under vacuum at 80 ° C and room temperature conditions while calcination at 300 ° C and 500 ° C with a heating rate <2 ° C/min in atmospheric. The CSZ gel diameter measured and the physical condition was observed by digital microscope. The result of measurement of wet CSZ gel diameter, the drying gel atdiameter is 1.0058 mm and the diameter of the calcined product at 300oC is 0.663 mm and 500oC is 0.635 mm. The physical condition of CSZ gel after dryingprocess and calcination shows intact, round and not cracked . Keywords: sol gel, external gelation, ceria stabilized zirconia

Item Type: Article
Subjects: Daur Bahan Bakar Nuklir dan Bahan Maju > Bahan Bakar Nuklir > Teknik Pemurnian dan Konversi Bahan Bakar Nuklir
Divisions: Pusat Teknologi Bahan Bakar Nuklir
Depositing User: USER PTBBN BATAN
Date Deposited: 17 May 2018 02:47
Last Modified: 17 May 2018 02:47
URI: http://repo-nkm.batan.go.id/id/eprint/1263

Actions (login required)

View Item View Item