ANALISIS KUALITAS SAMPEL LAS GTAW DENGAN METODA NDT

Mudi Haryanto, MH and S. Nitiswati, SN and Andryansyah, AD (2016) ANALISIS KUALITAS SAMPEL LAS GTAW DENGAN METODA NDT. In: Prosiding Seminar Nasional Teknologi Energi Nuklir 2016, 4-5 Agustus 2016, BATAM.

[img]
Preview
Text
PROSIDING_SENTEN_2016.pdf

Download (145MB) | Preview

Abstract

ABSTRAK ANALISIS KUALITAS SAMPEL LAS GTAW DENGAN METODA NDT . Pada umumnya bejana tekan reaktor nuklir dikonstruksi dengan cara dilas dengan proses Gas Tungsten Arc Welding (GTAW). Untuk keperluan penelitian yang akan dilakukan oleh peneliti lain tentang integritas baja karbon SA516 Gr.70 yaitu bahan bejana tekan HTR-10 yang mengalami pengelasan GTAW, akan dilakukan uji mekanik untuk benda uji las-lasan SA516 Gr.70. Persyaratan sebagai benda uji las-lasan SA516 Gr.70 yaitu harus mempunyai kualitas las- lasan yang baik, artinya harus bebas dari berbagai ketidaksinambungan las (discontinuity weld) akibat proses pengelasan antara lain porositas, retak, inklusi dan lain sebagainya. Sebelum benda uji las-lasan untuk pengujian mekanik dipabrikasi,perlu disiapkan terlebih dahulu bahan sampel uji las-lasan SA516 Gr.70 dengan persyaratan sama dengan persyaratan benda uji las-lasan. Penelitian ini tujuannya untuk mendapatkan bahan sampel uji las-lasan SA516 Gr.70 yang kualitasnya baik sehingga memenuhi persyaratan untuk digunakan sebagai bahan pembuatan benda uji mekanik las-lasan SA516 Gr.70. Sampel ini dibuat dengan ukuran 300 x 300 x16 mm sebanyak 3 sampel las GTAW yang diambil dari pelat baja SA516 Gr.70. Tahapan pengujian tak rusak (Non Destrctive Test/NDT) adalah mendeteksi kualitas permukaan las dengan metode dye penetran dan magnetik partikel sedangkan kualitas yang didalam (volumetric) las dengan metode ultrasonik dan radiografi. Dari hasil analisis, ke tiga sampel las GTAW dengan metode NDT tidak diterima sebagai bahan uji mekanik (uji rusak) karena tidak memenuhi syarat. Kata kunci : sampel las, GTAW, ketidaksinambungan, uji tak rusak, uji rusak ABSTRACT ANALYSIS OF GTAW WELD SAMPLE QUALITY WITH NDT METHODS . In general, the nuclear reactor pressure vessel is constructed in a manner welded with the Gas Tungsten Arc Welding (GTAW). For the purposes of the research to be conducted by other researchers about the integrity of the carbon steel SA516 Gr.70 ie material pressure vessel HTR-10 is experiencing GTAW welding, mechanical tests will be performed on the test specimen welds SA516 Gr.70. Terms as specimen welds SA516 Gr.70 which must have quality welds are good, that should be free of any discontinuity welding (weld discontinuity) as a result of the welding process include porosity, cracks, inclusions, and so forth. Before the test specimen welds for mechanical testing fabricated, need to be prepared in advance of the test sample material welds SA516 Gr.70 with the same requirements with the requirements of the test specimen welds. This research aim to obtain a test sample material SA516 Gr.70 welds are good quality so that it meets the requirements for use as materials for mechanical test specimen welds SA516 Gr.70. These samples were made with a size of 300 x 300 x16 mm by 3 samples taken from the GTAW welding steel plate SA516 Gr.70. Stages of nondestructive testing (NDT) is to detect surface quality welding method dye penetrant and magnetic particle while the quality of the inside (volumetric) welding by ultrasonic and radiographic methods. From the analysis, all three samples with the GTAW welding NDT methods are not accepted as a mechanical test (test broken) because it does not qualify. Keywords: welding samples, GTAW, discontinuity, nondestructive testing, destructive test

Item Type: Conference or Workshop Item (Paper)
Subjects: Keselamatan dan Keamanan Nuklir
Divisions: Pusat Teknologi dan Keselamatan Reaktor Nuklir
Depositing User: USER PTKRN BATAN
Date Deposited: 14 May 2018 07:53
Last Modified: 14 May 2018 07:53
URI: http://repo-nkm.batan.go.id/id/eprint/1547

Actions (login required)

View Item View Item