ANALISIS STRUKTUR MIKRO BAJA SA516Gr70 AKIBAT REGANGAN TARIK DAN MULUR

Andryansyah, AD and Sri Nitiswati, SN and Mudi Haryanto, MH and Darlis, DL (2016) ANALISIS STRUKTUR MIKRO BAJA SA516Gr70 AKIBAT REGANGAN TARIK DAN MULUR. In: Prosiding Seminar Nasional Teknologi Energi Nuklir 2016, 4-5 Agustus 2016, BATAM.

[img]
Preview
Text
PROSIDING_SENTEN_2016.pdf

Download (145MB) | Preview

Abstract

ABSTRAK ANALISIS STRUKTUR MIKRO BAJA SA516GR70 AKIBAT REGANGAN TARIK DAN MULUR . Telah dilakukan analisis terhadap bentuk struktur mikro baja SA516Gr70 akibat adanya regangan tarik yang disimulasikan dengan cara melakukan pengujian tarik dan regangan mulur dengan pengujian Creep . Tujuan dilakukannya penelitian ini adalah untuk dapat melihat langsung bagaimana perubahan butiran akan terjadi pada baja bila menerima regangan tarik atau mulur dan melihat perbedaannya. Dipilihnya baja dengan type SA516Gr70 karena baja ini banyak digunakan sebagai bahan pembuat bejana tekan, sehingga akan dapat dimanfaatkan pada inspeksi bejana tekan termasuk pada industri nuklir. Untuk mensimulasikan keadaan nyata pada baja yang mengalami peregangan tarik, maka dilakukan penarikan dengan tiga keadaan, yaitu ditarik hingga daerah elastik, ditarik hingga kekuatan maksimumnya, dan ditarik hingga terputus. Temperatur pengujian yang dipilih adalah 450 O C dengan harapan akan terjadi proses pemuluran pada uji Creep . Uji Creep dilakukan dengan waktu sekitar 115 dan 329 jam dengan beban dan temperatur yang sama dengan uji tarik. Dari hasil analisis yang dilakukan dapat disimpulkan bahwa struktur mikro pada baja SA516Gr70 yang mengalami regangan tarik tidak memperlihatkan batas butir ferit yang melebar, tetapi batas butir itu terlihat melebar pada spesimen yang mengalami regangan mulur Kata kunci: struktur mikro, SA516Gr70, uji tarik, regangan mulur. ABSTRACT MICROSTRUCTURE ANALYSIS OF STEEL SA516GR70 DUE TO TENSILE STRAIN AND CREEP . Analysis of the shape of the microstructure of steel SA516Gr70 due to tensile strain were simulated by means of tensile testing and creep strain. The purpose of this study is to see how the change will occur in the steel grains when it receives a tensile load or creep and what the differences are. Steel SA516Gr70 is chosen because the steel is widely used as material for pressure vessels. Therefore, the results can be used in the inspection of pressure vessels including nuclear industries. To simulate the real situation on the steel experiencing tensile strain, the specimens are prepared at three conditions. It was pulled to reach its elastic regim, to reach its maximum strength, and to reach its fracture limit. The test temperature was 450 O C to enable process of elongation on Creep Test. Creep test is conducted with approximately 115 and 329 hours with the same load and temperature as tensile test. From the results of the analysis, it can be concluded that microstructure of steel SA516Gr70 experiencing tensile strain does not show the ferrite grain boundary widening, but the grain boundary widen at the specimen experiencing creep strain. Keyword: microstructure, SA516Gr70, strain, tensile, creep.

Item Type: Conference or Workshop Item (Paper)
Subjects: Keselamatan dan Keamanan Nuklir
Divisions: Pusat Teknologi dan Keselamatan Reaktor Nuklir
Depositing User: USER PTKRN BATAN
Date Deposited: 14 May 2018 08:51
Last Modified: 14 May 2018 08:51
URI: http://repo-nkm.batan.go.id/id/eprint/1562

Actions (login required)

View Item View Item