Purwanto, S and Wisnu, A.A and Salim, M (2015) ENHANCEMENT OF GIANT MAGNETORESISTANCE IN Fe2O3-MWCNT/PVA NANOCOMPOSITE FILM. Jurnal Sains Materi Indonesia, 16 (3). pp. 97-101. ISSN 1411-1098

[img] Text
4225 - Published Version
Available under License Creative Commons Attribution Non-commercial Share Alike.

Download (24kB)


Synthesis and magnetic properties characterization of Fe2O3-MWCNT/PVA nanocomposite film were carried out. Fe2O3-MWCNT as a filler of nanocomposite thin film were synthesized using simple mixingmethods froma solution containing FeCl3, andMulti-Walled Carbon Nanotube (MWNT). The solution was sonicated for almost 20 minutes then dried at 450 oC for one hour. The mixture of the two composition was dispersed with Sodium Dodecyl Sulfate (SDS) in 20 mL aquabidest and homogenized by ultrasonicator for 15 minutes at 40 oC. Then filler was then mixed with Polyvinyl Alcohol (PVA) with some various concentration and dried overnight at room temperature. X Ray Diffraction (XRD) analysis and Raman Spectroscopy were used to find out the presence of Fe2O3 phase in as prepared sample. Iron oxide phase partially filled in the wall of MWCNT observed by Transmission Electron Microscope (TEM). The Giant Magnetoresistance (GMR) properties were investigated. The maximum GMR value was negative 80% of the composition 1:9 filler/matrix volume ratio. The linear negative of the magnetoresistance (MR) ratio is coincident with a model as proposed by Nguyen, Spivak and Shklovskii (NSS) and related to the effect of quantum interference between Fe2O3-MWCNT in PVA matrix.

Item Type: Article
Subjects: Daur Bahan Bakar Nuklir dan Bahan Maju
Daur Bahan Bakar Nuklir dan Bahan Maju > Bahan Struktur dan Bahan Maju
Divisions: Pusat Sains dan Teknologi Bahan Maju
Date Deposited: 16 May 2018 02:34
Last Modified: 18 May 2018 02:42
URI: http://repo-nkm.batan.go.id/id/eprint/1765

Actions (login required)

View Item View Item