PENGARUH TEMPERATUR DAN WAKTU HOMOGENISASI TERHADAP KARAKTERISTIK PELAT PADUAN AG3NE

Hadijaya, Hadijaya and Aidah, Siti and Masrukan, Masrukan (2018) PENGARUH TEMPERATUR DAN WAKTU HOMOGENISASI TERHADAP KARAKTERISTIK PELAT PADUAN AG3NE. Urania, 24 (2). pp. 73-84. ISSN 2528-0473

[img] Text (Jurnal Ilmiah Urania)
3897

Download (95kB)

Abstract

ABSTRAK PENGARUH TEMPERATUR DAN WAKTU HOMOGENISASI TERHADAP KARAKTERISTIK PELAT PADUAN AG3NE. Telah dilakukan penelitian mengenai pengaruh temperatur dan waktu homogenisasi terhadap karakteristik pelat paduan AG3NE. Paduan AG3NE merupakan paduan yang dapat digunakan sebagai kelongsong elemen bakar reaktor riset. Ingot hasil peleburan AlMgFeSi dicuplik untuk dilakukan beberapa pengujian diantaranya komposisi kimia, kekerasan, mikrostruktur, fasa, densitas dan korosi. Hasil pengujian komposisi kimia dipoeroleh unsur Al= 96,110%; Fe= 0,188%; Mg= 2,333 dan Si= 0,355%. Kekerasan AG3NE yang dikenai proses pendinginan cepat diperoleh sebesar 153,33 HV; sedangkan yang mengalami pendinginan lambat 72,70 HV, dan kekerasan paduan AlMgSi sebesar 79,30 HV. Hasil analisis mikrostruktur menggunakan mikroskop optik menunjukkan bahwa paduan AG3NE tanpa dihomogenisasi mempunyai bentuk butir pipih sebagian berbentuk dendrite dengan diameter butir rata-rata 0,02 mm sedangkan paduan AG3NE yang dihomogenisasi pada temperatur 500°C dengan variasi waktu selama 1 ; 2; 3 dan 4 jam mempunyai butir dengan diameter rata-rata berturut-turut sebesar 0,01 mm, 0,02 mm, 0,03 mm dan 0,04 mm. Hasil uji fasa menggunakan XRD diperoleh fasa Al (ά) dan fasa kedua FeSiAl5 yang terdapat pada sudut 2θ sebesar 38,24° dan 44,446° dengan hkl masing-masing (119) dan (209) serta mempunyai intensitas sinar sebesar 100% dan 76,6%. Sementara itu dari hasil pengukuran densitas AG3NE diperoleh densitas rerata yang hampir sama dengan paduan AlMgSi sebagai pembanding. Densitas paduan AG3NE diperoleh sebesar 2,6893 ± 0,0013 g/cm3 , sedangkan AlMgSi sebesar 2,6910 ± 0,0283 g/cm3 . Sementara itu, hasil uji korosi menunjukkan bahwa laju korosi paduan AG3NE lebih rendah dibandingkan dengan paduan AlMgSi. Hasil karakterisasi komposisi kimia, kekerasan mikro, mikrostruktur, densitas dan laju korosi dapat disimpulkan bahwa paduan AG3NE dapat digunakan sebagai kandidat kelongsong bahan bakar nuklir untuk reaktor riset. Kata kunci: Paduan AG3NE, AlMgSi, homogenisasi, karakterisasi, bahan struktur. ABSTRACT EFFECTS OF HOMOGENIZATION TEMPERATURE AND TIME ON THE CHARACTERISTICS OF AG3NE ALLOY PLATE. Investigation on the effects of homogenization temperature and time on AG3NE alloy plate has been done. AG3NE alloy is used as cladding material of research reactor fuel. Ingot of AlMgFeSi melt was sampled for several tests and examination such as chemical composition, hardness, microstructure, phase, density and corrossion. Composition analysis shows that the alloy is composed of Al= 96.110%, Fe= 0.188%, Mg= 2.333% and Si= 0.355%.The hardness value for AG3NE is 153.33 HV for samples treated with rapid cooling and 72.70 HV for samples treated with slow cooling. Microstructure examination with optical microscope shows that AG3NE alloy without homogenization consists of flat grains with a fraction of dendrite of 0.02 mm mean diameter, while samples homogenized at 500°C at varied temperatures of 1, 2, 3, and 4 hours consist of grains with 0.01 mm, 0.02 mm, 0.03 mm and 0.04 mm respectively.Phase analysis with X-Ray Difractometer indicates the existance of Al (ά) and FeSiAl5 phases at 2θ of 38.24° - hkl (119) and 44.446° - hkl (209) with 100% and 76.6% intensity respectively.The measured density of AG3NE, however, is similar to that of AlMgSi as material for comparison, the values of which are 2.6893 ± 0.0013 g/cm3 for AG3NE and 2.6910 ± 0.0283 g/cm3 for AlMgSi. Corrossion rate analysis shows that the corrossion rate for AG3NE is lower than that for AlMgSi. Based on the characterization for chemical composition, microhardness, microstructure, density and corrossion rate, it is concluded that AG3NE alloy can be used as a candidate for cladding material for research reactor fuel. Keywords: AG3NE, AlMgSi, homogenization, characterization, structural material.

Item Type: Article
Subjects: Daur Bahan Bakar Nuklir dan Bahan Maju > Bahan Bakar Nuklir > Teknik Sintesis Bahan Bakar Nuklir
Divisions: Pusat Teknologi Bahan Bakar Nuklir
Depositing User: USER PTBBN BATAN
Date Deposited: 13 Nov 2018 03:53
Last Modified: 13 Nov 2018 03:53
URI: http://repo-nkm.batan.go.id/id/eprint/4021

Actions (login required)

View Item View Item