RANCANGAN MODIFIKASI TEST SECTION SPESIMEN UJI TARIK PADA TEKANAN 180 BAR DENGAN TEMPERATUR 500 ºC

Dedy Haryanto, DH and inzar anas, ia and paidjo, pj (2008) RANCANGAN MODIFIKASI TEST SECTION SPESIMEN UJI TARIK PADA TEKANAN 180 BAR DENGAN TEMPERATUR 500 ºC. RANCANGAN MODIFIKASI TEST SECTION SPESIMEN UJI TARIK PADA TEKANAN 180 BAR DENGAN TEMPERATUR 500 ºC. pp. 220-227. ISSN ISBN 978-979-17109-3-0

[img]
Preview
Text
33_DedyH-PTRKN.pdf

Download (222kB) | Preview

Abstract

ABSTRAK RANCANGAN MODIFIKASI TEST SECTION SPESIMEN UJI TARIK PADA TEKANAN 180 BAR DENGAN TEMPERATUR 500 ºC. Telah dilakukan rancangan modifikasi test section (ruang uji) spesimen uji tarik yang mampu dioperasikan pada tekanan 180 bar dengan temperatur 500 ºC. Perancangan modifikasi ini bertujuan untuk meningkatkan kinerja ruang uji sebagai tempat perlakuan termohidrolik dengan temperatur tinggi pada spesimen uji tarik. Untuk mendapatkan temperatur yang tinggi sesuai dengan penelitian, maka ruang uji tersebut dicangkokkan pada Untai Uji Korosi (Primary Loop). Rancangan ruang uji diawali dengan menentukan ketebalan minimal pipa yang akan digunakan melalui suatu perhitungan. Dari hasil perhitungan pipa yang digunakan adalah pipa seamless berdiameter nominal 5” (127 mm) schedule 120 dan untuk menghubungkan dengan Untai Uji Korosi digunakan tube stainless steel seamless berdiameter 18 mm tebal 1,5 mm, pada bagian dalam ruang uji terdapat rod dan hanger. Selain meningkatkan tekanan dan temperatur disain modifikasi juga dilakukan pada hanger dengan menambahkan jumlah hanger sehingga masing-masing spesimen dijepit kedua ujungnya untuk menjaga kestabilan posisinya. Perancangan modifikasi ruang uji ini diharapkan dapat menjadi landasan untuk kegiatan pabrikasi ruang uji. ABSTRACT MODIFICATION DESIGN OF TEST SECTION FOR TENSILE TEST SPECIMEN AT 180 BAR WITH TEMPERATURE 500 ºC. Have been done of design for test section modification for tensile specimen capable to be operated at dividing valve of 180 bar with temperature 500º C. Design of modification aim to increase test section performance as place for treatment of thermo hydraulic with high temperature at tensile test specimen. To get high temperature so the shell can be transplanted to Circuit Test of Corrosion (Primary Loop). Design this shell are started by determining minimum thickness of pipe which will be applied through a calculation. From result of calculation, which pipe are applied is pipe seamless with nominal diameter 5" (127 mm) schedule 120 and to connected to Primary Loop is applied by tube stainless steel seamless is having diameter 18 mm with thickness 1,5 mm, at shell interior there is rod and hanger. Besides increasing design's pressure and temperature, this modification also have been done at hanger with adding number of hanger so that each specimen at both of the nose its bounded to take care of stability of its the position. Design of test section modification expected can become reference for activity of test section manufacturing

Item Type: Article
Subjects: Keselamatan dan Keamanan Nuklir
Divisions: Pusat Teknologi dan Keselamatan Reaktor Nuklir
Depositing User: USER PTKRN BATAN
Date Deposited: 14 Nov 2018 02:54
Last Modified: 14 Nov 2018 02:54
URI: http://repo-nkm.batan.go.id/id/eprint/5134

Actions (login required)

View Item View Item