Phase analysis and magnet properties of ZnxFe(3-x)O4 prepared by milling process

Mashadi, Mashadi and Tiana, Saskia and Yunasfi, Yunasfi (2018) Phase analysis and magnet properties of ZnxFe(3-x)O4 prepared by milling process. Malaysian Journal of Fundamental and Applied Sciences, 14 (2). pp. 208-212. ISSN 2289-599x

[img]
Preview
Text
940-4426-1-PB.pdf - Published Version
Available under License Creative Commons Attribution Non-commercial Share Alike.

Download (1MB) | Preview

Abstract

Phase analysis and magnetic properties of ZnxFe(3-x)O4 (x = 0,25; 0,50; 0,75 and 1,0) have been done. The synthesis of ZnxFe(3-x)O4 was carried out using a solid reaction with the xZnO : (3-x)Fe2O3 material composition (x = 0.25, 0.50, 0.75 and 1.0) according to the mole ratio of each, then milling for 5 hours and then sintered at a temperature of 1200 °C for 3 hours. Phase identification with XRD (X-ray Diffractometer) shows that ZnxFe(3-x)O4 milling results form the diffraction peak of the NiFe2O4 and Fe2O3 phases, the greater the value of x (the Zn atom content) the less Fe2O3 % phase while the % phase ZnFe2O4 is getting bigger and even for x = 1.0 only ZnFe2O4 phase is formed (ZnFe2O4 formed 100% or single phase). Surface morphological observations with SEM (Scanning Electron Microscope) show the formation of an increasingly homogeneous structure along with the addition of Zn2+ ion content and varying sizes ranging from 1 µm to 100 nm. The properties magnetic of ZnFe2O4 with VSM (vibrating sample magnetometer) showed that the sample behave ferromagnetically with Ms higher (in the range 1.89 - 21.10 emu/g) while the Hc value is smaller (in the range 243 - 107 Oe) with the addition of Zn2+ ion content. Thus, the presence of the Fe2O3 phase can decrease the magnetic properties of the material.

Item Type: Article
Subjects: Daur Bahan Bakar Nuklir dan Bahan Maju > Bahan Struktur dan Bahan Maju
Divisions: Pusat Sains dan Teknologi Bahan Maju
Depositing User: EDITOR PSTBM BATAN
Date Deposited: 14 Nov 2018 01:06
Last Modified: 14 Nov 2018 01:06
URI: http://repo-nkm.batan.go.id/id/eprint/5153

Actions (login required)

View Item View Item