PENGARUH ZINC TERHADAP LAJU KOROSI INCONEL 690 DAN INCOLOY 800 SEBAGAI MATERIAL TUBE PEMBANGKIT UAP PWR

Febrianto Bahar, FB (2010) PENGARUH ZINC TERHADAP LAJU KOROSI INCONEL 690 DAN INCOLOY 800 SEBAGAI MATERIAL TUBE PEMBANGKIT UAP PWR. PENGARUH ZINC TERHADAP LAJU KOROSI INCONEL 690 DAN INCOLOY 800 SEBAGAI MATERIAL TUBE PEMBANGKIT UAP PWR. pp. 302-306. ISSN 0854-2910

[img]
Preview
Text
392-396 Febrianto.pdf

Download (3MB) | Preview

Abstract

ABSTRAK PENGARUH ZINC TERHADAP LAJU KOROSI INCONEL 690 DAN INCOLOY 800 SEBAGAI MATERIAL TUBE PEMBANGKIT UAP PWR. Telah dilakukan pengujian untuk melihat pengaruh zinc terhadap laju korosi dan deposisinya pada permukaan Inconel 690 dan Incoloy 800 sebagai material tube pembangkit uap reaktor PWR (Pressurized Water Reactor /Reaktor Air Bertekanan). Pada reaktor PWR seperti juga pada reaktor BWR (Boiling Water Reactor/ Reaktor Air Mendidih) banyak ditemukan problem korosi. Pada reaktor BWR, penambahan zinc digunakan untuk menurunkan paparan radiasi tetapi dalam kenyataannya juga bisa menurunkan laju korosi dari material/komponen reaktor. Pengujian ini bertujuan untuk melihat sejauh mana peran zinc dalam menurunkan laju korosi dan dalam pembentukan oksida di permukaan material. Pengujian laju korosi dilakukan dengan Potensiostat dimana sebelumnya material yang diuji telah dikondisikan dengan menggunakan autoclave pada temperatur 250 o C selama 250 jam. Pada penelitian ini juga dilihat pengaruh zinc terhadap perubahan akumulasi kobalt pada permukaan material. Spesimen berbentuk tube dengan diameter luar 19,05 mm, tebal 1,09 mm dan panjang 10 mm. Dari hasil yang didapat, laju korosi material setelah penambahan zinc oksida lebih kecil dari pada sebelum penambahan zinc oksida. Oksida yang terbentuk dalam larutan kobalt sulfat lebih tebal dan tidak merata sedangkan oksida yang terbentuk setelah penambahan larutan zinc oksida terlihat lebih tipis dan merata. Dari hasil penelitian yang didapat, laju korosi Inconel 690 dalam larutan cobalt sulfat sebesar 1,9745 mpy dan laju korosi Incolloy 800 sebesar 1,6891 mpy. Sedangkan laju korosi Inconel 690 dalam larutan zinc oksida sebesar 0,5297 mpy dan laju korosi Incolloy 800 dalam larutan yang sama sebesar 0,4534 mpy. Kata kunci : laju korosi, tube pembangkit uap, autoclave ABSTRACT EFFECT OF ZINC ON INCONEL 690 AND INCOLOY 800 CORROSION RATE AS PWR STEAM GENERATOR TUBE MATERIAL. The experiment has been done to see the effect of zinc addition on corrosion rate and its deposition at Inconel 690 dan Incoloy 800 as PWR (Pressurized Water Reactor) steam generator material tube. At PWR and also BWR (Boiling Water Reactor) many corrosion problems have been found. At BWR , the purpose of zinc addition is for radiation exposure reducing but, in fact zinc addition can reduce material corrosion rate. The experiment purposes are to see the zinc role in reducing corrosion rate and oxide formation on material surface. The experiment carried out using autoclave at 250 o C for 250 hours and corrosion rate was determined by Potentiosatat. In this experiment, effect of zinc on cobalt accumulation change at material surface has been determined. The specimen is in tube form with 19,05 mm in diameter, 1,09 mm in thickness and 10 mm length. From experiment the results, material corrosion rate after zinc oxide addition smaller than that before zinc oxide addition. Oxide that form in cobalt sulphate solution was more thickness and not uniform also oxide that form after zinc oxide addition was thinner and uniform. From the experiment results; Inconel 690 corrosion rate in cobalt sulphate solution is 1,9745 mpy and Incolloy 800 corrosion rate is 1,6891 mpy. Inconel 690 corrosion rate in zinc oxide is 0,5297 mpy and Incolloy 800 corrosion rate is 0,4534 mpy in same solution. Keywords : corrosion rate, steam generator tube, autoclave

Item Type: Article
Subjects: Keselamatan dan Keamanan Nuklir
Divisions: Pusat Teknologi dan Keselamatan Reaktor Nuklir
Depositing User: USER PTKRN BATAN
Date Deposited: 14 Nov 2018 08:02
Last Modified: 14 Nov 2018 08:02
URI: http://repo-nkm.batan.go.id/id/eprint/5215

Actions (login required)

View Item View Item