PENGARUH FOSFOR TERHADAP KUAT TANGGUH BAJA FERITIK SEBAGAI MATERIAL BEJANA TEKAN REAKTOR NUKLIR

Sri Nitiswati, SN and Piping Supriatna, PS and Sumijanto, ST and Alim Mardhi, AM (2010) PENGARUH FOSFOR TERHADAP KUAT TANGGUH BAJA FERITIK SEBAGAI MATERIAL BEJANA TEKAN REAKTOR NUKLIR. PENGARUH FOSFOR TERHADAP KUAT TANGGUH BAJA FERITIK SEBAGAI MATERIAL BEJANA TEKAN REAKTOR NUKLIR. pp. 313-320. ISSN 0854-2910

[img]
Preview
Text
403-410 Sri Nitirwati.pdf

Download (5MB) | Preview

Abstract

ABSTRAK PENGARUH FOSFOR TERHADAP KUAT TANGGUH BAJA FERITIK SEBAGAI MATERIAL BEJANA TEKAN REAKTOR NUKLIR. Unsur fosfor (P) didalam baja feritik yang digunakan sebagai material bejana tekan reaktor nuklir harus dibatasi karena dalam jumlah tertentu, unsur P dapat mengakibatkan penggetasan batas butir sehingga kuat tangguhnya menurun, yang berarti pula keandalan dan integritas bejana tekan juga menurun. Perlu dilakukan suatu penelitian tentang pengaruh P terhadap kuat tangguh baja feritik, dengan mengoptimasi kandungan fosfornya. Tujuannya adalah mendapatkan kandungan P optimal yang berpengaruh terhadap kuat tangguh baja feritik. Metode yang digunakan adalah dengan melakukan serangkaian pengujian mekanik terhadap baja feritik yang mengandung 6 (enam) variasi kandungan unsur P. Pengujian mekanik meliputi impak charpy v-notch dengan jumlah benda uji masingmasing 3 buah untuk setiap varian dan setiap temperatur uji, pengukuran kekerasan dengan jumlah benda uji masing-masing 1 buah untuk setiap varian, uji tarik dengan jumlah benda uji masing-masing 3 buah untuk setiap varian, dan analisis bidang patahan serta melakukan evaluasi terpadu terhadap hasil-hasil pengujian. Berdasarkan hasil penelitian dan analisis disimpulkan bahwa baja feritik dengan kandungan unsur P optimal 0,0132% berat mempunyai kuat tangguh/ketangguhan patah yang sifatnya rapuh pada temperatur -320C. Kata kunci : kuat tangguh, baja feritik, bejana tekan nuklir. ABSTRACT EFFECT OF PHOSPHORUS ON FRACTURE TOUGHNESS OF FERRITIC STEEL AS NUCLEAR REACTOR PRESSURE VESSEL MATERIAL. Phosphorus (P) content in ferritic steel utilized as nuclear reactor pressure vessel material must be limited, because amount of certain P can caused intergranular embrittlement therefore decrease in toughness, it means reactor pressure vessel integrity and reliability also decrease. Research on effect of P on fracture toughness of ferritic steel needs to be performed through optimized of P content. Objective of the research is to obtain optimal P content that influence on fracture toughness of ferritic steel. The method was used through a series of mechanical testing to ferritic steel that contained 6 (six) P as variables. Mechanical testing covered charpy v-notch impact with amount of specimen was 3 pieces for each test temperature and variant, hardness measurement with amount of specimen was 1 piece for each variant, tensile test with amount of specimen was 3 pieces for each variant, analysis of fracture facet and evaluation of all test results. As conclusion that ferritic steel with optimal P content of 0.0132 % (weight) has brittle fracture toughness in -320C. Keyword : fracture toughness, ferritic steel, nuclear pressure vessel.

Item Type: Article
Subjects: Keselamatan dan Keamanan Nuklir
Divisions: Pusat Teknologi dan Keselamatan Reaktor Nuklir
Depositing User: USER PTKRN BATAN
Date Deposited: 14 Nov 2018 08:02
Last Modified: 14 Nov 2018 08:02
URI: http://repo-nkm.batan.go.id/id/eprint/5217

Actions (login required)

View Item View Item