Sintering Effect on the Microstructure And Magnetic Properties of Co-Alxoy Composite Compound

Mulyaningsih, Sri and Purwanto, Setyo and Mujamilah, Mujamilah and Adi, Wisnu Ari and Manaf, Azwar (2008) Sintering Effect on the Microstructure And Magnetic Properties of Co-Alxoy Composite Compound. IPTEK The Journal for Technology and Science, 19 (2). pp. 41-46.

[img] Text
154 - Published Version
Available under License Creative Commons Attribution Share Alike.

Download (32kB)

Abstract

Research on sintering effect on the micro structure and the magnetic properties of composite Co-AlxOy materials has been done. The experiment was carried out by high energy milling (HEM) to refine Co and Al sample powder, followed by sintering process. The composition of sample was Co73Al27 wt% with weight ratio to the ball was 1:2.7. The milling time was varied within 4.5, 12 and 20 hours, while sintering process was conducted at 384ºC and 484ºC. Several new peaks were found after sintering process and identified as a Co-Al2O4 compound. The experiment data shows the saturation magnetization Ms value was decline for the entire sample by the sintering process. The Mr value for the 12h milling was remind stable about 9 emu/gr but, for 4.5 milling was decline from 17.5 to 9.2 and 6.2 emu/gr , while for 20h milling from 13,5 to 9.25 and 8 emu/gr. No visible changes in the microstructure are observed.

Item Type: Article
Subjects: Daur Bahan Bakar Nuklir dan Bahan Maju > Bahan Struktur dan Bahan Maju > Teknik Sintesis Bahan Maju
Divisions: Pusat Sains dan Teknologi Bahan Maju
Depositing User: EDITOR PSTBM BATAN
Date Deposited: 29 Nov 2018 05:58
Last Modified: 29 Nov 2018 05:58
URI: http://repo-nkm.batan.go.id/id/eprint/5745

Actions (login required)

View Item View Item