Microstructural studies of nanocrystalline α-alumina powder produced from Al13-cluster

Harun Al Rashid Megat Ahmad, Megat and Aziz Mohamed, Abdul and Ibrahim, Azmi and Seman Mahmood, Che and Putra, Edy Giri Rachman and Jamro, Rafhayudi and Kasim, Razali and Rawi Muhammad Zin, Muhammad (2007) Microstructural studies of nanocrystalline α-alumina powder produced from Al13-cluster. Journal of Physics and Chemistry of Solids, 68 (12). pp. 2349-2352. ISSN 00223697

[img] Text
S0022369707003447 - Published Version
Available under License Creative Commons Attribution Non-commercial Share Alike.

Download (63kB)


Nanocrystalline alumina powder was produced from calcinations of Al13-oxalate precipitates at 1100 °C. A nearly normal distribution of agglomerated alumina powder was obtained with an average particle size of about 1 μm. XRD measurement confirmed that the alumina produced was of high purity and crystalline α-phase. Microstructural features of both the precipitates and alumina obtained were studied using the small angle neutron scattering (SANS) technique. SANS examinations show the formation of microstructures in the alumina powder of mass fractals type with dimension of ∼2.8 indicative of low intra-granular porosity.

Item Type: Article
Subjects: Daur Bahan Bakar Nuklir dan Bahan Maju > Bahan Struktur dan Bahan Maju > Teknik Sintesis Bahan Maju
Divisions: Pusat Sains dan Teknologi Bahan Maju
Date Deposited: 01 Dec 2018 11:51
Last Modified: 01 Dec 2018 11:51
URI: http://repo-nkm.batan.go.id/id/eprint/7222

Actions (login required)

View Item View Item