ANALISIS KOROSI MATERIAL TANGKI REAKTOR TRIGA MARK II BANDUNG

Febrianto Bahar, FB and Khairul, KH and Sriyono, SR and Puradwi I, Pur and W.Nur RaHMAH, WNR (2000) ANALISIS KOROSI MATERIAL TANGKI REAKTOR TRIGA MARK II BANDUNG. In: Prosiding Presentasi Ilmiah Teknologi Keselamatan Nuklir V, 28 Juni 2000, Prosiding Presentasi Ilmiah Teknologi Keselamatan Nuklir V P2TKN Serpong.

[img] Text (ANALISIS KOROSI MATERIAL TANGKI REAKTOR TRIGA MARK II BANDUNG)
pros-febrianal-2000a.PDF - Published Version
Restricted to Repository staff only

Download (20kB)

Abstract

ABSTRAK ANALISIS KOROSI MATERIAL TANGKI REAKTOR TRIGA MARK II BANDUNG. Telah dilakukan penelitian untuk melihat pengaruh pekerjaan las-lasan terhadap korosi material aluminium seri 6061. Untuk melihat pengaruh korosi terhadap material ini dilakukan dalam lingkungan larutan yang mengandung khlorida dengan metoda potensiodinamik. Dari hasil yang didapat terlihat adanya pengaruh pengelasan terhadap laju korosi pada material aluminium 6061. Dimana laju korosi semakin kecil bila semakin jauh dari daerah terpengaruh panas (HAZ, Heat Affected Zone). laju korosi semakin kecil. Laju korosi yang teramati adalah 0,000218 mpy pada daerah HAZ, 0,000130 mpy dan 0,000109 mpy pada daerah 1 cm dan 2 cm dari HAZ ABSTRACT ANALYSIS OF MATERIAL CORROSION ON REACTOR TANK OF TRIGA MARK II BANDUNG. The investigations to see effect of welding on corrosion rate of aluminium type 6061 has been done. The experiments were conducted in environment chloride containing solution by potentiodynamic method.From the experiment result shown hat welding had influenced on corrosion rate of aluminium tipe 6061. The corrosion rate is smaller in area further from HAZ compared than it near to heat affected zone. Corrosion rate was found namely 0.000218 mpy at HAZ area and 0.000130 and 0.000109 mpy at 1 cm and 2 cm from HAZ areas, consecutively. 68

Item Type: Conference or Workshop Item (Paper)
Subjects: Keselamatan dan Keamanan Nuklir
Divisions: Pusat Teknologi dan Keselamatan Reaktor Nuklir
Depositing User: USER PTKRN BATAN
Date Deposited: 04 Dec 2018 04:05
Last Modified: 04 Dec 2018 04:05
URI: http://repo-nkm.batan.go.id/id/eprint/7671

Actions (login required)

View Item View Item