ANALISIS KERUSAKAN PIPA BOILER INDUSTRI

M. Nasir, MNR and Soedarjo, SDR and B.Dewi Arhatari, BDA and Andryansyah, ADR and Sriyono, SR and Mudi Haryanto, MH and Ari Triyadi, AT (2000) ANALISIS KERUSAKAN PIPA BOILER INDUSTRI. In: Prosiding Presentasi Ilmiah Teknologi Keselamatan Nuklir V, 28 Juni 2000, Prosiding Presentasi Ilmiah Teknologi Keselamatan Nuklir V P2TKN Serpong.

[img] Text (ANALISIS KERUSAKAN PIPA BOILER INDUSTRI)
pros-natsir-2000a.PDF - Published Version
Restricted to Repository staff only

Download (402kB)

Abstract

ABSTRAK ANALISIS KERUSAKAN PIPA BOILER INDUSTRI. Telah dilakukan analisis kerusakan pipa boiler Industri. Material pipa yang diuji adalah jenis baja karbon SA 178 Grade A berdasarkan data spesifikasi yang diperoleh dari Pabrik pupuk. Tahaptahap yang dilakukan dalam analisis meliputi ; Pengumpulan latar belakang sejarah operasi dan spesifikasi bahan, pemeriksaan visual, uji dye penentrant, uji radiografi, uji komposisi kimia, uji kekerasan dan uji metalografi. Dari hasil analisis dan pengujian diketahui pipa tersebut mengalami penipisan ketebalan akibat erosi dan pada bagian lasan terdapat cacat porositas dan penetrasi tak penuh. Penyebab utama kerusakan pipa adalah erosi akibat kavitasi yang menyebabkan penipisan pada dinding pipa. Penipisan ini pada akhirnya menyebabkan kebocoran pada dinding pipa. Untuk mengatasi masalah ini, maka pipa tersebut harus diganti dengan pipa yang baru. ABSTRACT FAILURE ANALYSIS OF INDUSTRIAL BOILER PIPE. Failure analysis of industrial boiler pipe has been done. The tested pipe material is carbon steel SA 178 Grade A refer to specification data which taken from Fertilizer Company. Steps in analysis were ; collection of background operation and material specification, visual inspection, dye penetrant test, radiography test, chemical composition test, hardness test, metallography test. From the test and analysis result, it is shown that the pipe failure caused by erosion and welding was shown porosity and incomplete penetration. The main cause of failure pipe is erosion due to cavitation, which decreases the pipe thickness. Break in pipe thickness can be done due to decreasing in pipe thickness.To anticipate this problem, the pipe will be replaced with new pipe.

Item Type: Conference or Workshop Item (Paper)
Subjects: Keselamatan dan Keamanan Nuklir
Divisions: Pusat Teknologi dan Keselamatan Reaktor Nuklir
Depositing User: USER PTKRN BATAN
Date Deposited: 20 Dec 2018 02:37
Last Modified: 20 Dec 2018 02:37
URI: http://repo-nkm.batan.go.id/id/eprint/7954

Actions (login required)

View Item View Item