OPTIMASI PARAMETER PEMISAHAN Zr DALAM PEB U3Si2/Al PRA IRADIASI MENGGUNAKAN METODE KROMATOGRAFI PENUKAR ANION

Yanlinastuti, Yanlinastuti and Noviarty, Noviarty and Haryati, Iis and Fatimah, Syamsul and Boybul, Boybul and Br. Ginting, Aslina (2019) OPTIMASI PARAMETER PEMISAHAN Zr DALAM PEB U3Si2/Al PRA IRADIASI MENGGUNAKAN METODE KROMATOGRAFI PENUKAR ANION. Jurnal Ilmiah Daur Bahan Bakar Nuklir (URANIA) Vol 25, No 2 (2019), Juni 2019, 25 (2). pp. 93-102. ISSN p ISSN 0852−4777; e ISSN 2528−0473

[img] Text
5508

Download (63kB)

Abstract

OPTIMASI PARAMETER PEMISAHAN Zr DALAM PEB U3Si2/Al PRA IRADIASI MENGGUNAKAN METODE KROMATOGRAFI PENUKAR ANION. Telah dilakukan optimasi parameter pemisahan zirconium dalam larutan PEB U3Si2/Al pra iradiasi menggunakan metode kromatografi penukar anion dan analisisnya menggunakan spektrofotometer UV-Vis. Zirconium merupakan salah satu isotop yang dapat digunakan untuk penentuan burn-updalam bahan bakar, untuk mendapatkan hasil zirconium yang optimal perlu dipelajari parameter-parameter yang mempengaruhi terhadap pengukuran. Tujuan penelitian ini adalah untuk mendapatkan parameter optimal pemisahan zirconium dalam bahan standar maupun larutan PEB U3Si2/Al pra iradiasi menggunakan metode kromatografi penukar anion. Optimasi parameter pemisahan Zr dengan metode kromatografi penukar anion dilakukan menggunakan resin Dowex 1x-8 dengan variasi berat 0,5; 1,0; 1,5; 2,0 dan 2,5 g, keasaman umpan H2SO41; 2; 3; 4;5 dan 6M, konsentrasi umpan standar Zr dengan 50; 100 ; 150, dan 200 ppm dan kecepatan alir bahan elusi H2SO4 3 M pada 0,1; 0,3; 0,5; 0,7 dan 0,9 mL/menit. Efluen Zr sebagai hasil pemisahan ditambahkan Arsenazo III 0,1% sebagai pengompleks dan dilakukan analisis menggunakan spektrofotometer UV-Vis pada panjang gelombang 665,3 nm. Hasil pengukuran diperoleh parameter optimal pemisahan Zr pada penggunaan resin seberat 1,5 g dengan recovery 70,79 %, keasaman H2SO4 3M dengan recovery 83,94%, konsentrasi umpan sebesar 150 ppm dengan recovery 87,64% pada kecepatan alir pada 0,5 mL/menit. Parameter optimal ini digunakan untuk pemisahan unsur Zr di dalam larutan PEB U3Si2/Al pra iradiasi dan diperoleh recovery pemisahan sebesar 96,23%. Optimasi parameter metode kromatografi penukar anion yang diperoleh dapat digunakan untuk pemisahan unsur Zr dalam larutan PEB U3Si2/Al pasca iradiasi. Kata kunci : Parameter pemisahan, zirconium, PEB U3Si2/Al, kromatografi, penukar anion. ABSTRACT OPTIMIZATION OF PROCESS PARAMETERS OF Zr SEPARATION FROM U3Si2/Al FRESH FUEL BY ANION EXCHANGER CHROMATOGRAPHY. Determination of optimum parameters in the process of zirconium separation from U3Si2/Al fresh fuel solution by anion exchanger chromatography and analysis with UV-Vis spectrophotometer has been carried out. Zirconium is one of isotopes that can be used in the determination of fuel burn-up. The purpose of this study is to obtain optimal parameters of zirconium separation in standard materials as well as U3Si2/Al fresh fuel solution by anion exchanger chromatography. Optimization of Zr separation parameters was carried out using Dowex 1x-8 resin with a variation in weight of 0.5; 1.0; 1.5; 2.0 and 2.5 g, acidity of H2SO4 at 1 ; 2; 3; 4; 5 and 6 M, standard feed concentrations of Zr at 50; 100; 150 and 200 ppm and flow rate of 3M H2SO4 elution at 0.1; 0.3; 0.5; 0.7 and 0.9 mL/minute. To the Zr effluent as the result of separation was added Arsenazo III 0.1% as complexing agent, and subsequent analysis with UV-Vis spectrophotometry was done at a wavelength of 665.3 nm. The measurement results show that the optimal parameters of Zr separation are the use of 1.5 g resin with resulting recovery of 70.79%, acidity of 3M H2SO4 with recovery of 83.94%, feed concentration of 150 ppm with recovery of 87.64% at a flow rate of 0.5 mL/minute. When those optimal parameters were used in Zr separation from U3Si2/Al fresh fuel solution, the recovery obtained was 96.23%. These optimized parameters can also be used to separate Zr from U3Si2/Al irradiated fuel solution. Keywords: separation, zirconium, fuel element plate of U3Si2/Al, anion exchange chromatography

Item Type: Article
Subjects: Daur Bahan Bakar Nuklir dan Bahan Maju > Bahan Bakar Nuklir > Teknik Karakterisasi Bahan Bakar Nuklir
Divisions: Pusat Teknologi Bahan Bakar Nuklir
Depositing User: USER PTBBN BATAN
Date Deposited: 09 Sep 2020 04:33
Last Modified: 09 Sep 2020 04:33
URI: http://repo-nkm.batan.go.id/id/eprint/9302

Actions (login required)

View Item View Item