KARAKTERISASI MIKROSTRUKTUR, KEKERASAN, KOMPOSISI KIMIA DAN STRUKTUR KRISTAL LAPISAN PADA PERMUKAAN BAJA

Sungkono, Sungkono and Kartaman Ajiriyanto, Maman and Ismarwanti, Sri and Sigit, Rohmat (2019) KARAKTERISASI MIKROSTRUKTUR, KEKERASAN, KOMPOSISI KIMIA DAN STRUKTUR KRISTAL LAPISAN PADA PERMUKAAN BAJA. Jurnal Imliah Daur Bahan Bakar Nuklir Urania, 25 (3). pp. 165-172. ISSN p ISSN 0852−4777; e ISSN 2528−0473

[img] Text
5021

Download (59kB)

Abstract

KARAKTERISASI MIKROSTRUKTUR, KEKERASAN, KOMPOSISI KIMIA DAN STRUKTUR KRISTAL LAPISAN PADA PERMUKAAN BAJA. Baja dan paduannya digunakan sebagai bahan struktur komponen reaktor nuklir dan peralatan dukung fasilitas hot cell. Selama pengoperasian reaktor nuklir atau fasilitas hot cell, bahan struktur mengalami tegangan tarik, tekan, dan gesek dalam lingkungan radiasi tinggi sehingga dapat menurunkan umur komponen. Salah satu solusi yang digunakan adalah pelapisan permukaan baja dengan bahan pelapis yang mempunyai kekerasan, ketahanan korosi dan aus tinggi. Penelitian ini mempunyai tujuan untuk mendapatkan karakter mikrostruktur, ketebalan, kekerasan, komposisi kimia dan struktur kristal lapisan pada permukaan baja. Metode yang digunakan adalah pengamatan mikrostruktur menggunakan mikroskop optik, kekerasan dengan vickers microhardness tester, komposisi kimia dengan spark spectrometer dan struktur lapisan permukaan baja dengan difraktometer sinar-X (XRD). Hasil penelitian menunjukkan bahwa mikrostruktur base metal terdiri dari butiran ekuiaksial halus dengan fasa ferit dan perlit, antarmuka logam-lapisan terlihat jelas, serta lapisan kompak dan homogen dengan ketebalan rerata 624,071 m. Kekerasan lapisan adalah 943 VHN. Dari komposisi kimia diketahui base metal adalah baja karbon S45C, sedangkan lapisan permukaan berupa senyawa stabil khrom oksida (Cr2O3) dengan struktur kristal heksagonal. Kata kunci: lapisan permukaan, baja, mikrostruktur, kekerasan, komposisi kimia, struktur kristal. Urania Vol. 25 No. 3, Oktober 2019: 141−204 p ISSN 0852−4777; e ISSN 2528−0473 166 ABSTRACT CHARACTERIZATION OF MICROSTRUCTURE, HARDNESS, CHEMICAL COMPOSITION AND CRYSTAL STRUCTURE OF LAYERS ON STEEL SURFACE. Steel and alloys are used as structural material for nuclear reactor components and supporting equipments of hot cells. During the operation of nuclear reactors or hot cell facilities, structural materials suffer from tensile, compressive, and frictional stresses in high radiation environments and thus reduce the life time of the components. One solution for this issue is surface coating of steel with materials having high hardness, corrosion and wear resistance. The aim of this research is to obtain the characteristics of microstructure, thickness, hardness, chemical composition and crystal structure of layers on steel surface. The method used was observation with optical microscope for microstructure, vickers microhardness tester for hardness, spark spectrometry for chemical composition and X-ray diffractometry for crystal structure. The results shows that the base metal microstructure consists of fine equiaxial grains with ferrite and pearlite phases, where the metallayer interface is clearly visible, and the compact and homogeneous layer has an average thickness of 624.071 µm. The hardness of the layer is 943 VHN. From the chemical composition it is identified that the base metal is S45C carbon steel, and the surface layer is a stable compound of chromium oxide (Cr2O3) with hexagonal crystal structure. Keywords : surface layer, steel, microstructure,hardness,chemical composition, crystal structure.

Item Type: Article
Subjects: Daur Bahan Bakar Nuklir dan Bahan Maju > Bahan Bakar Nuklir > Teknik Sintesis Bahan Bakar Nuklir
Divisions: Pusat Teknologi Bahan Bakar Nuklir
Depositing User: USER PTBBN BATAN
Date Deposited: 09 Sep 2020 05:41
Last Modified: 09 Sep 2020 05:41
URI: http://repo-nkm.batan.go.id/id/eprint/9594

Actions (login required)

View Item View Item