SIFAT-SIFAT MEKANIK PIPA PENDINGIN PRIMER REAKTOR RISET BANDUNG PASKA IRRADIASI Histori, Renaningsih S., Sri Nitiswati, Ari Triyadi

Histori, HRI and Renaningsih setyo, RS and Sri Nitiswati, SN and Ari Triyadi, AT (2003) SIFAT-SIFAT MEKANIK PIPA PENDINGIN PRIMER REAKTOR RISET BANDUNG PASKA IRRADIASI Histori, Renaningsih S., Sri Nitiswati, Ari Triyadi. In: Prosiding Presentasi Ilmiah Teknologi Keselamatan Nuklir VIII ISSN No. 1410-0533, 26 dan 27 Pebruari 2003, Prosiding Presentasi Ilmiah Teknologi Keselamatan Nuklir VIII ISSN No. 1410-0533.

Full text not available from this repository.

Abstract

ABSTRAK SIFAT-SIFAT MEKANIK PIPA PENDINGIN PRIMER REAKTOR RISET BANDUNG PASKA IRADIASI. Telah dilakukan serangkaian pengujian terhadap potongan pipa pendingin primer reaktor riset Bandung. Pipa pendingin primer terbuat dari Al 6061-T6. Tujuan pengujian adalah untuk mengetahui perubahan sifat mekanik akibat proses penuaan setelah mengalami iradiasi selama 33 tahun. Pengujian yang dilakukan antara lain adalah pengamatan secara visual, pengukuran ketebalan, pengujian tarik, dan uji kekerasan. Dari hasil pengamatan dan pengujian menunjukkan bahwa terdapat deposit yang merupakan produk korosi pada permukaan dalam pipa Al 6061 T6, terjadi penipisan sebesar 0,2 mm, kuat tarik pipa (tensile strength) sebesar 293 MPa, dan kuat luluhnya (yield strength) sebesar 262 MPa. Bila data hasil pengujian tersebut dibandingkan dengan standar ASTM untuk material baru, maka kuat tarik dan tegangan luluhnya masih memenuhi standar ASTM, sedangkan kekerasannya mengalami penurunan yang tidak signifikan. ABSTRACT MECHANICAL PROPERTIES OF POST IRRADIATION PRIMARY COOLING PIPING OF BANDUNG RESEARCH REACTOR. Testing on primary coolant piping of research reactor Bandung have been done. Primary coolant piping were made from Al 6061-T6. The goal of theis activity is to investigate the mechanical properties changes caused by aging process after 33 years in irradiated. Type of testing i.e visual examination, thickness measurement, tensile and hardness test were done. The test data shown that there was a deposit at the inside surface of pipe, thickness decreased about 0,2 mm, tensile strength is 293 MPa, yield strength is 262 MPa, while the hardness is about 83 HRE (mean value). The test data than compared with ASTM standard. As the conclusion tensile and yield strength of pipe still fulfill the ASTM requirements, except the hardness is unsignificantly less/decreased.

Item Type: Conference or Workshop Item (Paper)
Subjects: Keselamatan dan Keamanan Nuklir
Divisions: Pusat Teknologi dan Keselamatan Reaktor Nuklir
Depositing User: USER PTKRN BATAN
Date Deposited: 21 Apr 2020 07:02
Last Modified: 21 Apr 2020 07:02
URI: http://repo-nkm.batan.go.id/id/eprint/9762

Actions (login required)

View Item View Item